Silicone rubber ADDV-25 BLUE (set of two components)
ADDV-25 BLUE is a pourable, addition-curing 2-component RTV silicone rubber particularly suitable for the reproduction of models with undercuts using polyurethane and epoxy resins.
- Superior flowability
- Fast, shrinkage-free vulcanization at room temperature
- Good tear strength and tear propagation strength
Processing
Mixing ratio: 1 : 1 component A : component B
Processing time (at 25 °C): approx. 30-50 minutes
Demouldable (at 25 °C): 4 - 5 h
No heat of reaction occurs during vulcanization so that even larger quantities (e.g. 10 kg) can be poured without the risk of overheating.
If heat is added during curing (e.g. in a heating cabinet or oven), the vulcanization time is reduced by half at a temperature increase of each 10 °C. The heat thus accelerates the cross-linking reaction. The maximum recommended curing temperature is 70 °C.
Please note:
- Cannot be processed with our Universal Colour Pastes.
- The air stirred in during mixing can be removed by vacuuming in a desiccator. This ensures that the silicone is free of air bubbles to the maximum.
- For all equipment and tools used, make sure that no other materials such as epoxy resins or condensation-curing silicones have been processed beforehand. Addition-curing silicones may react to impurities with curing problems.
Technical data:
Mixing viscosity: 3.000 ± 300 mPas
Shore A hardness: 25 ±2
Tensile strength: > 5.5 N/mm²
Elongation at break: ≥ 680 %
Tear resistance: > 29 N/mm
Linear shrinkage: ≤ 0.1 %
Color:
Component A: Translucent
Component B: Blue
Additional information:
Delivery:
As both component batches are matches to each other, we only supply complete batches. It is not possible to obtain individual deliveries of silicone and catalyst.
Packs of 0.5, 1, and 2 kg are supplied in squeeze bottles and 10 and 20 kg in PE canisters.
Customer information:
The release agent Semiperm™ Monofilm in combination with PARTALL® Coverall Film PVA is suitable as a safe release agent for silicone moulds. This combination of release agents provides a barrier layer so that casting with epoxy resins is also possible without any problems. The service life (durability) of the molds is significantly extended.
The release agent Semiperm™ Monofilm is applied with a brush. After flash-off, PARTALL® Coverall Film PVA is applied, also with a brush or sponge. For more information on processing, see the release agents.
PARTALL® Coverall Film PVA is transferred to the casting, washed off with water after demolding and reapplied before each impression.