External release agent for epoxy and polyester resins, PMMA and polyurethanes
- Easy to polish, soft release wax for spray application (max curing temperatures of 120 °C)
Suitable substrates: practically all smooth surfaces such as plastic (GFK), metal and glass, but also porous and absorbent materials such as wood, gypsum and moulded ceramics, if multiple coats are applied. However, absorbent surfaces are difficult to mould if the resin can flow into the pores and anchor mechanically.
Release Spray TRS is also ideal for making surfaces of silicone rubber wettable. In addition, the release spray acts as an insulating layer and extends the durability of molds, especially when working with epoxy resins.
The fine spray facilitates applications in complex, multi-angled moulds. The release spray can also be used as a sliding layer by multiple spraying without intermediate polishing. This is necessary, for example, when manufacturing wound components such as cylindrical tubes in order to be able to pull out the winding cores again.
Shake can well before use. Spray from a distance of 20 - 30 cm. In hard-to-reach areas, it is also possible to spray at an angle or overhead for short periods.
New moulds are treated 2 - 3 times, whereby each layer is polished by hand with a soft cotton cloth immediately after application. After complete drying, the film can no longer be polished without streaks.
Allow to flash off for approx. 30 minutes on silicone rubber, then the surface can be coated e.g. with EP gel coat without forming eyes.
Remnants in the mould can be removed with white spirit or mechanically with steel wool.
Density at 20 °C (DIN Norm 51757): 0.64 g/ml
Active ingredient content: 2.95 %.
Flash point: > -97 °C
Viscosity at 20 °C (outlet cup 4 mm DIN EN ISO 2431): < 59 sec
Storage temperature: between 10 °C and 30 °C