Elan-tech® ADH 891.892 NF Epoxy adhesive (dark grey), 400 ml (MR 2:1)

Elan-tech® ADH 891.892 NF from Elantas is a temperature-resistant high-performance adhesive based on epoxy resin for bonding CFRP and GFRP materials, wood, glass, ceramics, rigid foams, as well as FE and non-ferrous metals in automotive construction and sports equipment.

This high-performance adhesive is an unfilled and stable 2 component epoxy resin adhesive. The adhesive complies with RoHS (EU Directive 2002/95/EC) and RoHS Directive 2011/65/EU (RoHS 2).

Due to its thixotropic formulation thick, uneven and even vertical adhesive joints can be achieved.

• High lap shear strength (up to 39 MPa with CFK cured 2 h over 80 °C according to ASTM D 1002)
• Very high impact and peel strength
• Good thermal resistance
• Thixotropic formulation
• Low exothermic reaction and shrinkage
• Solvent-free

Processing:
Processing is very easy due to the application with a dosing gun. This also eliminates mixing errors. Elan-tech® ADH 891.892 NF cures at room temperature or elevated temperatures. Post-curing at elevated temperatures is required to achieve maximum temperature resistance.

Technical data (averages):
Processing time (25 °C): 135 minutes*
Processing time (25 °C, 40 mm, 100 ml): 15-25 minutes
Handling strength (23 °C)**: 4 hours
Viscosity: 300.000 to 550.000 MPas
Maximal gap fill: 5 mm
Colour: Dark grey
Elongation at break: 6 %
Heat resistance: 24 h / 23 °C = 60 °C; 2 h / 80 °C = 85 °C
Flexural strength: 80 MPa
Bending modulus: 2200 MPa
Tensile strength: 54 MPa
Compressive strength: 58 %

*2 mm application at 25 °C with good wetting of the surfaces to be bonded. The processing time is reduced accordingly for thicker coatings and the resulting exothermic (reaction heat).
** Curing time until a minimum tensile shear strength of 1 MPa is reached on aluminum.

Please order the dosing gun for 400 ml double cartridges (MR 2:1) (Order no 153997-1) separately.

References of the boat building industry:
Wally Europe (Italy & Tunisia), the Baglietto Group (Cantieri di Pisa, W.Magic, General Bateaux), Comar (Italy), Indiana Yachting (Italy), CMR (Italy), Cantieri Soleri (Italy), Cantieri Galetti (Italy)

References of the automobile industry:
Ferrari (Italy), Dallara (Italy), Camattini Meccanica (Italy), Škoda (Czech Republic), Fiat (Italy), Volkswagen (South Africa), TataMotors (India)

Conversion of SI units: 1 MPa (Megapascal) = 1 N/mm² = 0,102 kg/mm²