Epoxy Resin L 20 + Hardener EPH 161 (90 Minuten), set of two components
- Low-viscosity, free of solvents and fillers
The combination of Epoxy Resin L 20 and Hardener EPH 161 yields a low-viscosity laminating resin that exhibits superior impregnating and wetting properties to glass, aramid, and carbon fibres.
In conjunction with Epoxy ResinL 20, Hardener EPH 161 results in a long service life for the resin compound with very high mechanical and dynamic strengths and perfect curing in both thick (> 2 cm) and thin (1,5 mm) laminates.
Before they can obtain the specified mechanical properties, the laminates must be post-cured for about 15 hours at 100 °C after their initial cold-curing period.
Processing time: 90 minutes
100 : 25 parts by weight of resin to hardener
100 : 29 parts by volume of resin to hardener
24 hours at room temperature, subsequent warm curing optional
Maximum distortion temperature:
Approx. 70 °C at 23 °C (up to a maximum of 120 °C with additional 15 h heat curing at 100 °C)