Epoxy Resin L + Hardener S (15 min)

Set of two components

Free from nonylphenol, benzyl alcohol and DETA
Low viscosity, solvent- and filler-free
Fast impregnation of glass, aramid and carbon fibres
High static and dynamic strength
Low surface tension, good adhesion and low curing shrinkage
Ideal for bonding wood, metal, Styropor® etc.

Epoxy resin L with the corresponding hardeners is the most frequently used laminating and bonding resin from the R&G product range.

Epoxy resin L with Hardener S has similar mechanical properties to the laminating systems commonly used in aircraft construction.

Processing time: 15 minutes (100 g / 20 °C)

Mixing ratio:
100 : 40 parts by weight Epoxy Resin L : Hardener S
100 : 45 parts by volume Epoxy Resin L : Hardener S

Curing time (at 23 °C): 16 - 24 hours
Cold hardening, hardens from 5 °C (low temperature hardener)
Heat distortion temperature: Approx. 65 °C

Processing:
It can be processed in all common processes such as hand lamination, pressure and vacuum impregnation as well as pressing and winding.

Material characteristics (pure resin cured) Epoxy Resin L with Hardener S:

Flexural strength DIN EN ISO 178 in MPa	110
Bending E-modulus DIN EN ISO 178 in MPa	--
Tensile strength DIN EN ISO 527 in MPa	68
Compressive strength DIN EN ISO 14126 in MPa	116

CYTOX expert opinion on the Resin System Epoxy Resin L + Hardener S (see below under additional information): this system is not cytotoxic (cell-damaging), important for applications in medical technology.

all Prices price incl. VAT, possibly plus shipping

Article information

MSDS Epoxy Resin L (PDF)

MSDS Hardener S (PDF)

Processing information Epoxy resin systems (PDF)

CYTOX Test Report (PDF)

Technical Data Sheet Epoxy Resin L and Hardeners (PDF)

Hazards identification - Epoxy Resin L

Hazard components for labelling

2,2'-[(1-methylethylidene)bis(4,1-phenyleneoxymethylene)] bisoxirane
1,6-bis(2,3-epoxypropoxy)hexane
Reaction mass of 2,2'-[methylenebis(4,1-phenyleneoxymethylene)]dioxirane and [2-({2-[4- (oxiran-2-ylmethoxy)benzyl]phenoxy}methyl)oxirane and [2,2'-[methylenebis(2,1-phenyleneoxymethylene)]dioxirane

Signal word: Warning

Pictograms:

Hazard statements

H315	Causes skin irritation.
H317	May cause an allergic skin reaction.
H319	Causes serious eye irritation.
H411	Toxic to aquatic life with long lasting effects.
H412	Harmful to aquatic life with long lasting effects

Precautionary statements

P261	Avoid breathing dust/fume/gas/mist/vapours/spray.
P273	Avoid release to the environment.
P280	Wear protective gloves / protective clothing / eye protection / face protection.
P305 P351 P338	IF IN EYES: Rinse continuously with water for several minutes. Remove contact lenses if present and easy to do. Continue rinsing.
P501	Dispose of waste according to applicable legislation.

Special labelling of certain mixtures

EUH205

Contains epoxy constituents. May produce an allergic reaction.

Hazards identification - Hardener S

Hazard components for labelling

1,3-Benzoldimethanamine
Salicylic acid
2,2,4-trimethylhexane-1,6-diamine
Reaction products of the oligomerization andalkylation of 2-phenylpropene and phenol
Reaction mass of (1-phenylethyl)phenols and bis-(1-phenylethyl)phenols

Signal word: Danger

Pictograms:

Hazard statements

H302	Harmful if swallowed.
H314	Causes severe skin burns and eye damage.
H317	May cause an allergic skin reaction.
H361d	Suspected of damaging the unborn child.
H411	Toxic to aquatic life with long lasting effects.

Precautionary statements

P303 P361 P353	IF ON SKIN (or hair): Remove/Take off immediately all contaminated clothing. Rinse skin with water or shower.
P305 P351 P338	IF IN EYES: Rinse continuously with water for several minutes. Remove contact lenses if present and easy to do. Continue rinsing.
P310	Immediately call a POISON CENTER or doctor / physician.
P362 P364	Take off contaminated clothing and wash it before reuse.
P405	Store locked up.
P501	Dispose of waste according to applicable legislation.